UV-HK688
UV/Visible light cure 紫外/可见光固化
encapsulating Adhesive 密封胶粘剂
PRODUCT DESCRIPTION 产品介绍
UV-HK688 is a one component, UV curable encapsulating adhesive. The material cures fast when exposed to 365 nm light. The cured film displays good humidity resistance, excellent high temperature and thermal shock stability, solvent resistance, good toughness. The application include sealant, coating and encapsulation of electronic devices to circuit boards and semiconductors (transistors, watch IC, etc.) it is a UV curing sealant system to save energy and time for high speed production。UV-HK688是一种单组分,UV固化密封胶粘剂。该产品可在365nm紫外光辐照下快速固化。固化后的材料膜层具有优良的耐潮性能,卓越的耐高温和热冲击稳定性,不溶解性和高粘接性。它可用于电子元器件到电路板及半导体(晶体管,集成电路)的密封,涂覆和封装。UV-HK688是一种用于高速生产上节省能量消耗和时间的UV固化密封材料。
PROPERTIES OF UNCURED MATERIAL 固化前材料性能
Property性能 |
Test Method测试方法 |
Value数值 |
Color/Appearance 颜色/外观 |
Visual 目测 |
Transparent, clear liquid
清澈透明液体 |
Specific Gravity 比重, 25 °C, g/cm3 |
ASTM D-792 |
1.1
|
Viscosity 粘度, cps, 25 °C, |
Brookfield RVT 布氏粘度 #2, 20 rpm |
800 – 1200 |
Refractive index 折射率 |
|
1.47 |
Shelf life 储存期@20 °C, month |
|
12 |
TYPICAL PROPERTIES OF CURED MATERIAL 固化后材料典型物理性能
Material cured at 30 sec x 100 mW/ cm2 材料在30 秒 x 100 mW/ cm2下固化
Property 性能 |
Test Method 测试方法 |
Value 数值 |
Hardness硬度 |
Shore D 邵氏硬度 |
70 |
Refractive index 折射率 |
|
1.51 |
Fixture time, glass slide 固定时间,玻璃片 |
6 mW/ cm2 |
10 seconds |
Yellowing resistance at 140℃
140℃下黄化时间 |
Continuous exposure
连续辐照 |
10 days
10天 |
Tensile strength 拉伸强度, N/mm2 |
ASTM D882 |
16 |
Tensile elongation,拉伸延长率 % |
ASTM D882 |
10 |
Chemical resistance
耐化学腐蚀性 |
3 minutes 3分钟 @ RT
Isopropanol 异丙醇(IPA)
Acetone 丙酮 |
No effect 无影响
No effect 无影响 |
Adhesion 粘附性 |
|
Good (Aluminum) 优异(铝)
Excellent (Cu) 极佳(铜) |
Dielectric strength 绝缘强度, kv /mm |
ASTM D149 |
20 - 29 |
Surface resistivity, Ω |
ASTM D257 |
1.5 E+15 |
Volume resistivity, Ω.CM |
ASTM D257 |
5.8 E+14 |
Dielectric constant/Dissipation factor |
ASTM D150 |
5.3/0.05 (1 kHz) |
|
|
4.1/0.05 (10 kHz) |
Hydrolytic stability 水解稳定性 |
Temperature and UV lamp 高温和UV灯
85 ℃ x 168 hours
100℃ x 168 hours |
No effect 无影响
No effect 无影响 |
DIRECTIONS FOR USE 使用指南
The adhesive can be hand applied from bottle, or dispensing systems are also available for high volume assembly applications. 该产品可手工从瓶中取出使用,对于大体积的装配生产可提供分散系统。
CURING TIME TABLE 固化进度表
The material cures when exposed to ultraviolet radiation and/or visible light with sufficient intensity. Recommended intensity for cure is 40 mW/ cm2 at 365 nm with exposure time of 4 – 5 times the fixture time at the same intensity. For dry curing of exposed surfaces, higher intensity UV is required, e.g. 100 mW/ cm2 minimum. 在足够强度的紫外和(或)可见光辐照下该产品可固化。推荐固化光强度为40mW/ cm2 at 365 nm,所需时间为相同光强下初固时间的4-5倍。对于外露表面的干养护,推荐使用更高强度的紫外光,如至少100 mW/ cm2。
STORAGE INFORMATION 储存方法
Store at 8 – 20 °C in a dry, cool place and in sealed containers out of direct sunlight. 在8 – 20 °C下干燥,凉爽和密封保存,避免阳光的直接照射。
Notes 注意: it is the user’s responsibility to determine the suitability of the products and methods of use. 用户具有决定产品的适用性和选择合适的使用方法的责任。
|